Ecosmart 801 series - inorganic anti-rust coat
Simply
coating without derust operation could have better performance
than organic one
Product Description:
Ecosmart inorganic anti-rust paint consists of inorganic nano-polysiloxane
resin and a new anti-rust pigment. It is a new ferrous anti-rust
paint which is easy to apply and has top adhesiveness and anti-rust
characteristics . It will be the substitute of organic coat
like lead red and resin coat etc.
1¡¢Specifications:
£¨1£©Direct coating using Escomart 801 Series paint without
the need
for a "derusting process".
£¨2£©Inorganic product are durable performance, no chalking
and
decolorization.
£¨3£©Acid resistance, alkali resistance, corrosion prevention.
£¨4£©Non-poisonous, no pollution..
£¨5£©Fire retardation up to 800 degrees, the paint will not
be distruct by cutting or welding.
£¨6£©No special storage requirement but venting.
2¡¢Typical Uses: Ferrous metal surface for anti-rust treatments.
3¡¢Methods of application:
£¨1£©Use steel brush to remove the oxidized rust and old paint
film on the basis material before application (rust can be
not completely removed)
£¨2£©Stir thoroughly before coating£»
£¨3£©Methods of application: by brush, roller and spraying.
£¨4£©Colour: Wide range of colors are available, including metal
color. Please refer to
Rotol standard colour chart.
4¡¢Colours: Wide range of colours.
5¡¢Technical information:
£¨1£©No flare point after solidifying
£¨2£©Drying time:20 min normal temperature 25¡æ£¬ 3hr normal temperature
25¡æ£¬
requires 7 days complete solidifying£¨25¡æ£©.
£¨3£©Specific gravity:0.9-1.0
£¨4£©Viscosity:50-55KU
£¨5£©Film thickness£¨Ò»µÀ£©:Wet film:70Um. Dry film:20--30Um
£¨6£©Hardness:0.58
£¨7£©Solid by volume:35-45©‡
£¨8£©Theoretical coverage:4-8©O/Kg.
£¨9£© Thinning and cleaning agent: isopropanol, methanol and
alcohol
£¨10£©
Storage : Three to six months under Rotol standard (normal
temperature 25¡æ)
6¡¢Environment targets:
£¨1£© Benzene, toluene, xylene, total ethylbenzene content:
none (national standard¡Ü500)
£¨2£© Halogenerated hydrocarbon content: none (national standard¡Ü500)
£¨3£© Formaldehyde and formaldehyde polymer content: less than
10 (national standard¡Ü100)
£¨4£© Heavy metal lead content: 1(national standard¡Ü90)
£¨5£© Heavy metal cadmium content: 2(national standard¡Ü75)
£¨6£© Heavy metal chrome content: none(national standard¡Ü60)
£¨7£© Heavy metal mercury content: none(national standard¡Ü60)
7£®Precautions to take note during application:
£¨1£© Avoid all contact any organic solvent or oils.
£¨2£© Spray equipments should be thoroughly cleaned by alcohol
before application.
£¨3£© Stir thoroughly before coating.
£¨4£© Avoid use under high humidity conditions. (eg; cloudy
or rainy days is not suitable
for application.)
£¨5£© Surface to be coated should be cleaned without dust and
oil.
£¨6£© Inflammable.
£¨7£© Avoid any contact with eyes or skins.